Local, small scale short-circuits in liquid metal batteries
When cycling liquid metal batteries, local short circuits have been observed several times. They manifest e.g. in the cell voltage. Fig. 1. shows one example: the sudden drop of the terminal voltage is a clear evidence of a short circuit of the battery. At the same time, a certain increase in cell temperature might be observed.
After dismantling used cells, the cathode metal can sometimes be found attached to the anode current collector. Fig. 2 shows one example: the small metallic deposits are in fact a mixture of Li and Bi. During normal operation, such effects should not occur. They can only be explained by small, localised short-circuits.
Such small-scale short-circuits can, amongst others, be explained by insufficient wetting of the current collector by the molten metal. Fig. 3 shows one example: as the molten Li does not wet the wire, large Li-droplets form. If these droplets grow too much, they might induce local short-circuits.
Publications
- Bénard, S.; Weber, N.; Horstmann, G.M.; Landgraf, S.; Weier, T.
Anode-metal drop formation and detachment mechanisms in liquid metal batteries
Journal of Power Sources 510(2021) 230339(2)
Content from Sidebar
URL of this article
https://www.hzdr.de/db/Cms?pOid=64127
Links of the content
(1) | https://www.hzdr.de/db/!ContMan.Visi.Card?pNid=no&pUser=7190 |
(2) | https://doi.org/10.1016/j.jpowsour.2021.230339 |