Mineral: |
Illite |
Reference: |
ML91 |
SCM Type: |
TL - Triple Layer
(C1: 2.4 F/m2, C2: 0.2 F/m2) |
Ionic Strength: |
|
Site Type: |
»Al-OH |
PZC: |
|
pK1: |
|
| |
pK2: |
7.5 |
| |
Site Density in nm-2: |
|
Original Site Density: |
|
Solid/Liquid Ratio in g/L: |
10.0 |
pH Range: |
|
Temperature in K: |
|
Method for Site Density: |
Method for Protolysis: | Not Specified |
Fit Method: |
Comment: |
raw data from [RSBM81]; CEC in [RSBM81]=10.1meq/100g; The total number of sites, NS, to be used in the modelling, was calculated from the reported cation exchange capacities and mass of clay present in the solution; the allocation of the site types (»SOH/»TOH) to silanol/aluminol sites was carried out with respect to the reference [R82a] |
|
Mineral: |
Illite |
Reference: |
ML91 |
SCM Type: |
TL - Triple Layer
(C1: 2.4 F/m2, C2: 0.2 F/m2) |
Ionic Strength: |
|
Site Type: |
»Si-OH |
PZC: |
|
pK1: |
1.1 |
| |
pK2: |
5.7 |
| |
Site Density in nm-2: |
|
Original Site Density: |
|
Solid/Liquid Ratio in g/L: |
10.0 |
pH Range: |
|
Temperature in K: |
|
Method for Site Density: |
Method for Protolysis: | Not Specified |
Fit Method: |
Comment: |
raw data from [RSBM81]; CEC in [RSBM81]=10.1meq/100g; The total number of sites, NS, to be used in the modelling, was calculated from the reported cation exchange capacities and mass of clay present in the solution; the allocation of the site types (»SOH/»TOH) to silanol/aluminol sites was carried out with respect to the reference [R82a] |
|