Transition from antiferromagnetic ground state to robust ferrimagnetic order with Curie temperatures above 420 K in manganese-based antiperovskite-type structures
Zhang, X.; Yuan, Q.; Gao, T.; Ren, Y.; Wu, H.; Huang, Q.; Zhao, J.; Wang, X.; Yuan, Y.; Xu, C.; Hu, Y.; Dynes, J. J.; Zhou, J.; Zhou, S.; Liu, Y.; Song, B.
Manganese (Mn)-based antiperovskite structures (Mn3AX, where A and X represent the 3d transition-metal elements and N or C atoms, respectively) have attracted growing attention because of their novel electronic and magnetic properties. However, the lack of an effective approach to regulate the magnetic coupling in Mn3AX crystal structure, particularly in antiferromagnetic ground states, hinders their further design and applications. Herein, robust high-temperature ferrimagnetic order with a Curie temperature (TC) in the range of B390–420 K was successfully achieved in Mn3GaxNx (x = 0.5, 0.6, and 0.7) via composition-deficient engineering. A systematic investigation, including synchrotron X-ray diffraction, neutron powder diffraction, pair distribution function, X-ray absorption near-edge structure, magnetic characterization, and first-principles calculations, convincingly indicated that the redistribution of partial atoms in the antiferromagnetic ground state was responsible for the observed long-range magnetic order. These results not only provide a new perspective into the design and construction of high-temperature ferrimagnets based on the Mn3AX structure, but also open up a promising avenue for the further design of Mn3AX-based spintronic or other multifunctional devices.
Journal of Materials Chemistry C 6(2018)48, 13336-13344
Cited 5 times in Scopus