1 PublicationIon Beam Modification of ZnO Epilayers: Sequential Processing
Turos, A.; Ratajczak, R.; Mieszczynski, C.; Jozwik, P.; Stonert, A.; Prucnal, S.; Heller, R.; Skorupa, W.; von Borany, J.; Guziewicz, E.
Defect agglomeration in ion-implanted compound semiconductors produces lattice stress eventually causing plastic deformation at sufficiently high fluence. Consequently, a dislocations tangle is formed which can hardly be completely removed by thermal annealing. To solve this problem, a new method of sequential processing has been developed consisting of low fluence ion implantation followed by subsequent annealing. The procedure can be then repeated until the required impurity concentration has been reached without producing excessive damage. Epitaxial ZnO layers are grown using the atomic layer deposition (ALD) technique. Structural changes in ZnO epilayers due to Yb-ion implantation and subsequent annealing are analyzed by Rutherford backscattering/channeling (RBS/c) and photoluminescence (PL). Correlation between defect transformations and PL efficiency is determined. Increased Yb-atom optical activation upon sequential processing as compared to the standard single-step annealing is observed.
Keywords: ZnO; ALD; Defects; ion implantation; RBS
Involved research facilities
- Ion Beam Center DOI: 10.17815/jlsrf-3-159
Related publications
- DOI: 10.17815/jlsrf-3-159 is cited by this (Id 28574) publication
-
Physica Status Solidi (A) 215(2018), 1700887
DOI: 10.1002/pssa.201700887
Cited 7 times in Scopus
Downloads
Permalink: https://www.hzdr.de/publications/Publ-28574