Properties of Common Structure Materials

Element  abundance  σn(barn)  σγ, tot (mbarn)  SN (MeV)
Li  7.500%  0.039  1.91  5.66
Li  92.50%  0.045  1.15  7.25
Li  nat  100%  <7.13>
Be  100.0%  0.008  2.52  1.67
10  19.90%  0.500  3.69  8.44
11  80.10%  0.005  2.93  11.5 
nat  100%  <10.89> 
12  98.90%  0.003  1.47  18.7
13  1.100%  0.001  5.72  4.95
nat  100%  <18.55>
O 16 8 99.76% 0.0002 ? 15.7
O 17 8 0.038% 0.24 ? 4.14
O 18 8 0.200% 0.0002 ? 8.04
O nat 8 100% - - <15.68> 
Al  27  13  100.0%  0.230  6.77  13.1
Cr  50  24  4.345%  16.00  13.0
Cr  52  24  83.78%  0.800  12.0
Cr  53  24  9.501%  18.00  7.94
Cr  54  24  2.365%  0.360  9.72
Cr  nat  24  100%  <11.60>  
Fe  54  26  5.800%  2.700  13.4
Fe  56  26  91.72%  2.600  11.2
Fe  57  26  2.200%  2.500  7.65
Fe  58  26  0.280%  1.300  10.0
Fe  5nat  26  100%  <11.25>  
Ni  58  28  68.08%  4.600  12.2
Ni  60  28  26.23%  2.900  11.4
Ni  61  28  1.140%  2.500  7.82
Ni  62  28  3.634%  15.00  10.6
Ni  64  28  0.926%  1.500  9.66
Ni  nat  28  100%  <11.86>  
Cd 110 48 12.5% 11.0 ? ?
Cd 111 48 12.8% 12.0 ? ?
Cd nat 48 100% - - ?
Pb 206 82 24.1% 0.03 2.909 8.10
Pb 207 82 22.1% 0.70 2.718 6.70
Pb 208 82 52.4% 0.0005 2.636 7.40
Pb nat 82 100% - - <7.31>  

Content of several types of steel

Quality groups

Deutsche Werkstoff-Nr 
DIN
USA-Code

AISI

Chemical composition (DIN 17440/41) (average values %)
      C Cr Ni Mo Ti
Ferritic chromium steels 1.4016 430 0.05 17 - - -
A2-Group (V2A) 1.4301 304 0.06 18 9 - -
1.4306 304L max.0.03 19 11 - -
1.4541 321 0.07 18 10 - 0.04
 
A4-Gruppe (V4A) 1.4401 316 0.06 17 12 2.3 -
1.4435 316L max.0.03 17 13 2.7 -
1.4571 316Ti 0.07 17 12 2.3 0.4