Controlling blue-violet electroluminescence of Ge-rich Er-doped SiO2 layers by millisecond annealing using flash lamps


Controlling blue-violet electroluminescence of Ge-rich Er-doped SiO2 layers by millisecond annealing using flash lamps

Kanjilal, A.; Rebohle, L.; Voelskow, M.; Helm, M.; Skorupa, W.

Systematic evolution of the 400 nm electroluminescence (EL) with increasing flash lamp annealing (FLA) temperature from 800 to 1100 °C in an Er-doped Ge-rich metal-oxide semiconductor structure is presented. No significant change in the 1535 nm Er EL is observed with increasing FLA temperature. Enhancement of the 400 nm EL decay time with rising FLA temperature is found to be associated with recrystallization of the damaged Ge clusters in the absence of Ge outdiffusion. The 400 nm EL quenching with continuous charge injection process is also discussed within the device operation time.

Keywords: electroluminescence; flash lamp annealing; Er-doped Ge-rich metal-oxide semiconductor

Related publications

Permalink: https://www.hzdr.de/publications/Publ-14361
Publ.-Id: 14361