Nanoindentation-induced pile-up in hydrogenated amorphous silicon


Nanoindentation-induced pile-up in hydrogenated amorphous silicon

Pantchev, B.; Danesh, P.; Wiezorek, J.; Schmidt, B.

Nanoindentation-induced material extrusion around the nanoindent (pile-up) leads to an overestimation of elastic modulus, E, and nanohardness, H, when the test results are evaluated using the Oliver and Pharr method. Factors affecting the pile-up during testing are residual stresses in film and ratio of film and substrate mechanical properties. Nanoindentation of hydrogenated amorphous silicon (a-Si:H) films has been carried out with the aim to study the effect of residual compressive stress on the pile-up in this material. To distinguish the contribution of compressive stress to the appearance of pile-up ion implantation has been used as a tool, which reduces the compressive stress in a-Si:H. Scanning probe microscope has been used for the imaging of the indent and evaluation of the pile-up. The values of E and H have been obtained from the experimental load-displacement curves using depth profiling with Berkovich tip, which has created negligible pile-up. A sharper cube corner tip has been used to study the pile-up. It has been established that pile-up is determined by the material plasticity, when the compressive stress is below 200 MPa. The contribution of mechanical stress to the pile-up is essential for the stress as high, as about 500 MPa.

Keywords: Nanoindentation; silicon hardness; ion implantation

Related publications

  • Lecture (Conference)
    16 th International School on Condensed Matter Physics “Progress in Solid State and Molecular Electronics, Ionics and Photonics”, 29.08.-03.09.2010, Varna, Bulgaria
  • Open Access Logo Journal of Physics: Conference Series 253(2010), 012054
    DOI: 10.1088/1742-6596/253/1/012054
    Cited 4 times in Scopus

Permalink: https://www.hzdr.de/publications/Publ-14867
Publ.-Id: 14867