Effect of Ga+ irradiation in molecular-beam epitaxy grown Pt/Co/Pt thin films studied by magneto-optic spectroscopy


Effect of Ga+ irradiation in molecular-beam epitaxy grown Pt/Co/Pt thin films studied by magneto-optic spectroscopy

Jakubisova-Liskova, E.; Visnovsky, S.; Wawro, A.; Baczewski, L. T.; Mazalski, P.; Maziewski, A.; Liedke, M. O.; McCord, J.; Fassbender, J.

In-depth profile changes induced by Ga+ ion irradiation in Pt(5 nm)/Co(3.3 nm)/Pt(20 nm)/Mo(20 nm) sandwiches MBE grown on Al2O3 substrates are deduced from complex magneto optic polar Kerr effect (PMOKE) measurements at photon energies between 1 and 5 eV. The Ga+ irradiation stimulate a redistribution of Pt and Co and leads to broadening of alloyed regions at Pt Co and Co Pt interfaces, which is evaluated using PMOKE spectra. The effect of four Ga+ fluences D between zero and 6×1015 Ga+/cm2 was studied. The observed PMOKE azimuth rotation peak centered at 4.5 eV reaches the maximum of 0.42 degree at D=1×1015 Ga+/cm2 and becomes thus enhanced by a factor of 3.2 with respect to that in the non-irradiated sample. At D=6×1015 Ga+/cm2 the peak amplitude falls to 0.05 degree. To find the in-depth profile of Co concentration s in the sandwiches as a function of D, the PMOKE azimuth rotation and ellipticity spectra are compared with a multilayer model, where ideal flat interfaces are replaced by sequences of CosPt1-s layers. The dependence on D is compared with that evaluated by simulation of the structural effects of ion irradiation. At the highest D, the irradiation produces an almost complete erosion of the top Pt and Co accompanied by mixing at the Pt-Mo interface.

Keywords: MBE; ion irradiation; PMOKE; CoPt

Related publications

Permalink: https://www.hzdr.de/publications/Publ-19973
Publ.-Id: 19973