Thermodynamics Behavior of Germanium During Equilibrium Reactions between FeOx-CaO-SiO2-MgO Slag and Molten Copper


Thermodynamics Behavior of Germanium During Equilibrium Reactions between FeOx-CaO-SiO2-MgO Slag and Molten Copper

Reuter, M. A.; Shuva, M. A. H.; Rhamdhani, M. A.; Brooks, G. A.; Masood, S.

The distribution ratio of germanium (Ge), (Formula presented.) during equilibrium reactions between magnesia-saturated FeOx-CaO-SiO2 (FCS) slag and molten copper has been measured under oxygen partial pressures from 10−10 to 10−7 atm and at temperatures 1473 to 1623 K (1200 to 1350 °C). It was observed that the Ge distribution ratio increases with increasing oxygen partial pressure, and with decreasing temperature. It was also observed that the distribution ratio is strongly dependent on slag basicity. The distribution ratio was observed to increase with increasing optical basicity. At fixed CaO concentration in the slag, the distribution ratio was found to increase with increasing Fe/SiO2 ratio, tending to a plateau at (Formula presented.) = 0.8. This behavior is consistent with the assessment of ionic bond fraction carried out in this study, and suggested the acidic nature of germanium oxide (GeO2) in the slag system studied. The characterisation results of the quenched slag suggested that Ge is present in the FeOx-CaO-SiO2-MgO slag predominantly as GeO2. At 1573 K (1300 °C) and (Formula presented.) = 10−8 atm, the activity coefficient of GeO2 in the slag was calculated to be in the range of 0.24 to 1.50. The results from the current study suggested that less-basic slag, high operating temperature, and low oxygen partial pressure promote a low Ge distribution ratio. These conditions are desired for maximizing Ge recovery, for example, during pyrometallurgical processing of Ge-containing e-waste through secondary copper smelting. Overall, the thermodynamics data generated from this study can be used for process modeling purposes for improving recovery of Ge in primary and secondary copper smelting processes.

Keywords: Engineering controlled terms: Copper; Germanium; Germanium oxides; Iron oxides; Magnesia; Oxygen; Partial pressure; Pyrometallurgy; Secondary recovery; Slags; Temperature; Thermodynamics; Distribution ratio; Equilibrium reactions; High operating temperature; Low oxygen partial pressure; Oxygen partial pressure; Pyrometallurgical processing; Secondary copper smelting; Thermodynamics data

Permalink: https://www.hzdr.de/publications/Publ-24040
Publ.-Id: 24040