Role of impurities and dislocations for the unintentional n-type conductivity in InN

We present a study on the role of dislocations and impurities for the unintentional n-type conductivity in high-quality InN grown by molecular beam epitaxy. The dislocation densities and H profiles in films with free electron concentrations in the low 10¹⁷ cm^-3 and mid 10¹⁸ cm^-3 range are measured, and analyzed in a comparative manner. It is shown that dislocations alone could not account for the free electron behavior in the InN films. On the other hand, large concentrations of H sufficient to explain, but exceeding substantially, the observed free electron densities are found. Furthermore, enhanced concentrations of H are revealed at the film surfaces, resembling the free electron behavior with surface electron accumulation. The low-conductive film was found to contain C and it is suggested that C passivates the H donors or acts as an acceptor, producing compensated material in this case. Therefore, it is concluded that the unintentional impurities play an important role for the unintentional n-type conductivity in InN. We suggest a scenario of H incorporation in InN that may reconcile the previously reported observations for the different role of impurities and dislocations for the unintentional n-type conductivity in InN.