Small-angle neutron scattering investigation of as-irradiated, annealed and reirradiated reactor pressure vessel weld material of decommissioned reactor

Small-angle neutron scattering (SANS) was applied to characterize the microstructure of weld material taken from the reactor pressure vessel (RPV) of the decommissioned VVER440(230)-type nuclear power plant (NPP) Greifswald, units 1, 2 and 4. The welding seam of highest neutron exposure of unit 1 was subject to a large-scale annealing treatment in 1988 after about 11.5 effective years of operation. The same type of annealing was applied to unit 2 in 1990 after about 11 effective years of operation. After final decommissioning of NPP Greifswald in 1990, RPV material was left in the reirradiated condition (unit 1), in the as-annealed condition (unit 2) and in the as-irradiated condition (unit 4). Trepans of material from the highly irradiated RPV welds of these units have recently become available for examination. The results of the SANS investigation are reported and compared with published results obtained for asirradiated, post-irradiation annealed and reirradiated surveillance material of the same type. We have found general agreement indicating in particular the formation of irradiation-induced Cu-enriched clusters and efficient recovery as a result of the largescale annealing treatments. The only essential difference was observed for the ratio of magnetic and nuclear scattering indicating differences of the cluster composition for the RPV wall and surveillance material.