Optical and microstructural properties of self-assembled InAs quantum structures in silicon

The InAs quantum structures were formed in silicon by sequential ion implantation and subsequent thermal annealing. Two kinds of crystalline InAs nanostructures were successfully synthesized: nanodots (NDs) and nanopyramids (NPs). The peaks at 215 and 235 cm−1, corresponding to the transverse optical (TO) and longitudinal optical (LO) InAs single-phonon modes, respectively, are clearly visible in the Raman spectra. Moreover, the PL band at around 1.3 μm, due to light emission from InAs NDs with an average diameter 7 ± 2 nm, was observed. The InAs NPs were found only in samples annealed for 20 ms at temperatures ranging from 1000 up to 1200°C. The crystallinity and pyramidal shape of InAs quantum structures were confirmed by HRTEM and XRD techniques. The average size of the NPs is 50 nm base and 50 nm height, and they are oriented parallel to the Si (001) planes. The lattice parameter of the NPs increases from 6.051 to 6.055 Å with the annealing temperature increasing from 1100 to 1200°C, due to lattice relaxation. Energy dispersive spectroscopy (EDS) shows almost stoichiometric composition of the InAs NPs.