Influence of the Irradiation Temperature on the Formation of Defects in Reactor Pressure Vessel Steels
Influence of the Irradiation Temperature on the Formation of Defects in Reactor Pressure Vessel Steels
Große, M.; Hempel, A.; Böhmert, J.; Brauer, G.; Haggag, F. M.
Two heats of reactor pressure vessel steel type A533-B-1 differing in their Cu content (0.07 and 0.14 wt.-%) were irradiated to a fluence of 1x1018 neutrons/cm2 at temperatures of 60, 121, and 288 °C, respectively. Their microstructure has been studied by SANS, SAXS, and PAS in the as-irradiated and post-irradiation annealed stages and compared to the behaviour of unirradiated material and the results are discussed.
-