Redox-Active Metaphosphate-Like Terminals Enable High-Capacity MXene Anodes for Ultrafast Na-Ion Storage

2D transition metal carbides and/or nitrides, so-called MXenes, are noted as ideal fast-charging cation-intercalation electrode materials, which nev-ertheless suffer from limited specific capacities. Herein, it is reported that constructing redox-active phosphorus−oxygen terminals can be an attractive strategy for Nb4C3 MXenes to remarkably boost their specific capacities for ultrafast Na+ storage. As revealed, redox-active terminals with a stoichio-metric formula of PO2- display a metaphosphate-like configuration with each P atom sustaining three PO bonds and one PO dangling bond. Compared with conventional O-terminals, metaphosphate-like terminals empower Nb4C3 (denoted PO2-Nb4C3) with considerably enriched carrier density (four-fold), improved conductivity (12.3-fold at 300 K), additional redox-active sites, boosted Nb redox depth, nondeclined Na+-diffusion capability, and buffered internal stress during Na+ intercalation/de-intercalation. Consequently, com-pared with O-terminated Nb4C3, PO2-Nb4C3 exhibits a doubled Na+-storage capacity (221.0 mAh g-1), well-retained fast-charging capability (4.9 min at 80% capacity retention), significantly promoted cycle life (nondegraded capacity over 2000 cycles), and justified feasibility for assembling energy−power-balanced Na-ion capacitors. This study unveils that the molecular-level design of MXene terminals provides opportunities for developing simulta-neously high-capacity and fast-charging electrodes, alleviating the energy−power tradeoff typical for energy-storage devices.