The beneficial role of flash lamp annealing on the epitaxial growth of the 3C-SiC on Si

For the realization of good quality 3C-SiC films epitaxially grown on Si the perfection of the film during the early stage of growth is substantial. In this paper the beneficial role of Flash Lamp Annealing (FLA) for the elimination of the defects in the SiC film and the strain reduction at the SiC/Si interface is discussed. FLA is a highly transient process, having a flash duration of a few milliseconds. When the energy density is sufficient high, it melts the silicon at the SiC/Si interface increasing the temperature there well above the melting point of the silicon. The melted Si dissolves the 3C-SiC near the interface. Additionally, the uppermost part of the 3C-SiC film is annealed due to the heat dissipation during the flash duration and the solidification of the molten region. During the solidification of the C-rich Si melt SiC grows by liquid phase epitaxy at the annealed uppermost 3C-SiC film which act as a seed. This process results in a substantial improvement of the SiC film, eliminating also the cavities and the stress at the interface.