Correlation between PIII nitriding parameters and corrosion behaviour of austenitic stainless steel

In this work, nitrogen plasma immersion ion implantation (PIII) treatment of austenitic stainless steels 1.4301 and 1.4571 was performed to investigate the influence of the process conditions on the corrosion properties. Short treatment, high voltage and high temperature result in a decreased corrosion potential while no correlation to layer thickness, nitrogen concentration or lattice expansion was found. Except for the possibility of small CrN agglomerates at high temperatures, no direct explanation for the results can be provided and it is argued that intrinsic stress accumulation and relaxation may be responsible.